Glo-Protek High Built Epoxy Zinc Rich Primer 2601
A two pack polyamide cured high built epoxy based Zinc Rich Primer to give approx 75% zinc contents and give excellent protection to steel.
TYPICAL USES :
Glo-Protek EPOXYY ZINC-RICH PRIMER 2601 is a high-performance primer to give maximum protection as part of any anti-corrosive coating system for aggressive environments like on off shore structures, petrochemical facilities, bridges and power plants. It is designed to provide excellent corrosion resistance in both maintenance and new construction situations.
TECHNICAL DATA :
| Colour | Grey |
|---|---|
| Finish | Matt finish |
| Volume solids | Approx. 48% |
| Recommended DFT/Coat | 25-50 microns per coat |
| Mixing Ratio | 3 : 1 by volume |
| Pot Life | 4-6 hours (30ºC) |
| Nozzle Orifice | 0.017" - 0.019" |
| Theoretical spreading rate | 14.00 - 7.40 sqm at above DFT |
| Surface Dry | 1 - 1.5 hours at 30ºC |
| Hard Dry | 4 hours |
| Fully cured | 7 days at 30ºC |
| Over coating Interval | Min: 24 hours; Max: 7 days |
| Flash point | 29ºC |
| Thinner | Epoxy thinner |
| Dry heat Resistance | Upto 30ºC (Intermittent) |
SURFACE PREPARATION
Surface coat to be dry and free from all surface contaminations. Preferably to be blast cleaned to Sa 2½ of Swedish specification. If blast cleaning is not possible, remove loose contaminations by power/hand tools.